Effect of Surface Processing Variables on Hydrogen Embrittlement of Steel Fasteners

Book excerpt: "Incremental step load testing was used in accordance with ASTM F1940 to rank a number coating processes used in the fastener industry for their propensity to cause internal hydrogen embrittlement. The results showed that coating permeability has a first order effect, while the quantity of hydrogen introduced by the process has a second order effect. Pure zinc electroplating processes, alkaline and acid, were found to be the most embrittling, owing to the low permeability of zinc. The least embrittling processes were zinc-nickel, alkaline and acid, owing to the high permeability of Zn-Ni coatings. Non-electrolytic processes, namely phosphating, mechanical galvanising, DacrometRTM and Magni 555RTM were found to be non-embrittling. Hot dip galvanising was found to be highly embrittling, evidently due to trapped hydrogen being released by the thermal shock of up-quenching upon immersion in molten zinc. The full effect of up-quenching on the metallurgical and mechanical properties of high strength steel requires further investigation." --